2014 Aluminum sheet plate is an Al-Cu-Mg-Si series high-strength wrought aluminum alloy, the copper content between 3.9% and 5.0%, can be strengthened by heat treatment. The chemical composition of 2014 alloy is similar to 2A14 aluminum alloy, it has high strength and good hot workability, and is easy to forge. The performance is basically the same as 2A14. Due to the high copper content of 2014 aluminum sheet, the strength is high, corrosion resistance is poor, and it is prone to intergranular corrosion and stress corrosion, the aluminum plate can be clad with pure aluminum to enhance its corrosion resistance. Its weldability and cutting performance are still good.Click to Order
Alloy | 2014 aluminum sheet plate |
Temper | F, O, H112, T3, T4, T42, T62, T6, T351, T651, etc. |
Thickness (mm) | 1.0-600 |
Width (mm) | 500-2650 |
Length (mm) | 500-16000 |
Application | Automobile molds, aluminum molds, precision molds, shoe molds, high-strength parts, heavy forgings, etc. |
Chemical composition:
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Zr |
Others |
AL |
|
2014 |
0.50-1.20 |
0.70 |
3.90-5.00 |
0.40-1.20 |
0.20-0.80 |
0.10 |
0.25 |
0.15 |
- |
Single |
Total |
Balance |
0.05 |
0.15 |
Mechanical properties:
Alloy & Temper |
Tensile strength Rm/Mpa |
Yield strength Rp0.2/Mpa |
Elongation % |
Hardness HBWα |
2014-T4 |
440 |
280 |
10 |
120 |
2014-T6 |
≥440 |
≥390 |
≥6 |
111 |
2014 aluminum plate is used in occasions requiring high strength and hardness (including high temperature), such as: molds, high-strength machine parts, heavy forgings, thick plates and extruded materials, wheels, truck frames and suspension system parts, etc.