1060-O aluminum plate, 1060-H24 aluminum plate, 1060-H14 aluminum plate, 1060-H18 aluminum plate

• * 1060 aluminum plate

1060 aluminum plate/aluminum strip, with an aluminum content of more than 99.60%, is the most common series of aluminum plate and strip products.

Advantages of 1060 aluminum plate: the production process is relatively simple, the technology is relatively complete, and the price is greatly advantageous compared to other high-end aluminum alloy aluminum plates. It has excellent tensile strength and compressive strength, and most of them can meet the basic production and processing requirements (stamping, drawing) and have strong formability. The original coil aluminum material used for transformer aluminum strip is 1060 pure aluminum plate as the main raw material.

1060 aluminum plate contains 0.05% copper, so its conductivity is 55%. The strength of 1060 aluminum plate is relatively low, and most of it is pure aluminum alloy profiles with various tempering conditions, such as O (annealed), H12, H14, H16, H18, etc. Flait Aluminum has multiple annealing furnace production lines, which can customize aluminum plates of different alloy states according to requirements. The hardness material data meets the standards. Among them, 1060-O aluminum plates can be stamped, deep drawn, etc.

• * 1060-O aluminum plate

1060-O aluminum plate is a special annealing process. Usually, O-temper aluminum plate refers to a complete annealing process of 1060 aluminum plate after its own extension processing.
However, it is called soft aluminum plate after the annealing process. Its process is actually basically the same as H24, H14, and H16. The annealing time of different 1060-O aluminum plates is longer. Because it is called soft aluminum plate, it is also a similar annealing process with low tensile strength. However, there are advantages and disadvantages. After the annealing time is extended, the elongation will be higher, which is more suitable for products with higher processing requirements for forming performance, such as pots, kitchen utensils, basins, and other mesh products.

1060-O aluminum plate, 1060-H24 aluminum plate, 1060-H14 aluminum plate, 1060-H18 aluminum plate

• 1. 1060-H18 pure aluminum plate

In the entire 1060 pure aluminum plate process, the H18 alloy temper is a relatively hard product in the entire use. Therefore, it is not suitable for bending, because the excellent performance of its process is that it has both aluminum content and hardness. It is generally suitable for products that do not bend but have high electrical conductivity requirements. Therefore, 1060-H18 pure aluminum plate is also a non-annealing aluminum plate processing technology.

• 2. 1060-H24 pure aluminum plate

The more commonly used 1060 aluminum plate annealing process is the H24 temper, which has the advantages of 90-degree bending without opening, high electrical conductivity, bendable, corrosion resistance and many other advantages. At the same time, in our current sales docking production process, it is a product with a relatively large overall sales volume. The application function field is also a relatively wide one.

• 3. 1060-H14 pure aluminum plate

H14 is relatively rare in the processing technology of 1060 pure aluminum plate, and is mainly used in the field of curtain wall aluminum plate processing. Therefore, it is still suitable for use in product series with high requirements for plate shape and hardness. Mainly 1100 aluminum plate, but many friends who are engaged in import and export foreign trade processing technology are beginning to choose H14 annealing pure aluminum plate processing technology.

• 4. 1060-O pure aluminum plate

In the industry, shallow punching or simple punching generally chooses 1060-H24 and H14 as the main tempers. However, if it is deep punching or spinning process, it is recommended to choose 1060-O state aluminum plate. At the same time, the processing technology of 1060-O aluminum plate is a type of aluminum plate processing technology with complex annealing process and long time. The average annealing time is about 20 hours, so it is relatively soft.